The bottom cloth of Tricot Interlining is divided into woven and knitted fabrics, and knitted linings are also called knits. Generally, there are two types of knitted interlinings, they are two way stretch interlining and four way elastic fusible interfacing and the width of the lining is usually 110cm and 150cm.The woven interlining cloth now coated with PA powder. In the past, the market used powder gum, its features is that need more glue and production process is simple.
The disadvantage is because of the large amount of glue, which is easy to seep glue, so it has been eliminated.At present, the most advanced technology is the double sided fusible process of non-foundation pulp, which is characterized by easy control of the amount of glue added, strong adhesion, resistance to washing and other special treatment. Now it is used by most manufacturers. The spinning interlining has strong tension and good elasticity.Collar interlining refers to a kind of adhesive lining used on the collar of a garment. It is also divided into shirt collar lining and suit collar interfacing.
The linings are usually made of T/C and pure cotton linings (also known as cotton linings) , which usually have HDPE, LDPE, PA and EVA coating.The processing technology of collar lining is mainly used scattering powder coating, and the coating is divided into point glue and plain glue. Point glue has convex concave and strong grain feeling with hand touching. The plain glue are smooth and reflective to the light. The softness of the same collar product can be adjusted by the resin.
Cotton woven fusible interfacing is coated with high temperature permanent adhesive powder, which is special for high-grade shirt collar and not blister after water wash. There are three kinds of hand feeling for choice which can match more requirements.Because the clothing fabric has the heat shrinkable property, we must pay attention to the fabric shrinkage in the selection of the collar interfacing, should choose the thickness and shrinkage rate similar to the fusible interlining, otherwise, there will be blistering and drop phenomenon.